Single-site pyrrolic-nitrogen-doped sp2-hybridized carbon materials and their pseudocapacitance

ABSTRACT Integrating nitrogen species into _sp_2-hybridized carbon materials has proved an efficient means to improve their electrochemical performance. Nevertheless, an inevitable mixture

of nitrogen species in carbon materials, due to the uncontrolled conversion among different nitrogen configurations involved in synthesizing nitrogen-doped carbon materials, largely retards

the precise identification of electrochemically active nitrogen configurations for specific reactions. Here, we report the preparation of single pyrrolic N-doped carbon materials (SPNCMs)

with a tunable nitrogen content from 0 to 4.22 at.% based on a strategy of low-temperature dehalogenation-induced and subsequent alkaline-activated pyrolysis of 3-halogenated

phenol-3-aminophenol-formaldehyde (X-APF) co-condensed resins. Additionally, considering that the pseudocapacitance of SPNCMs is positively dependent on the pyrrolic nitrogen content, it

could be inferred that pyrrolic nitrogen species are highly active pseudocapacitive sites for nitrogen-doped carbon materials. This work gives an ideal model for understanding the

contribution of pyrrolic nitrogen species in N-doped carbon materials. SIMILAR CONTENT BEING VIEWED BY OTHERS SYNTHESIS OF POLYPYRROLE/NITROGEN-DOPED POROUS CARBON MATRIX COMPOSITE AS THE

ELECTRODE MATERIAL FOR SUPERCAPACITORS Article Open access 21 September 2020 GRAPHITIC PHOSPHORUS COORDINATED SINGLE FE ATOMS FOR HYDROGENATIVE TRANSFORMATIONS Article Open access 13 August

2020 SYNERGISTIC EFFECT OF PEROVSKITES AND NITROGEN-DOPED CARBON HYBRID MATERIALS FOR IMPROVING OXYGEN REDUCTION REACTION Article Open access 13 November 2023 INTRODUCTION Carbon-based

nanomaterials exhibit versatile flexibility in their fundamental properties, such as their mechanical, thermal, optical, and electrical properties, which are dependent on the hybridization

of carbon, including _sp_3, _sp_2, and _sp_1,2,3,4,5,6,7,8. Doping heterogenous atoms, including nonmetal atoms (e.g. B, N, O, S, and P)9,10,11 and metal atoms (e.g. Pt, Fe, Co, Ni, Zn, and

Mo)12,13,14,15,16, into the framework of carbon-based nano materials could further tailor their fine electron structure to enhance their performance in the field of energy storage and

conversion. In particular, facilely doping nitrogen species into _sp_2-hybridized carbon materials has been proved to be efficient to improve their performance17,18,19 in electrochemical

fields, such as pseudocapacitance20,21, oxygen reduction reaction (ORR)22,23,24,25, CO2 reduction reaction26,27,28, oxygen evolution reaction (OER)29,30,31, hydrogen evolution reaction

(HER)32, nitrogen reduction reaction33,34,35, and so on, mainly because nitrogen doping could tailor local electron structures and/or induce substitutional defects of carbon materials,

thereby enhancing their intrinsic chemical activities and/or increasing the number of active sites. To further develop high-performance nitrogen-doped _sp_2-hybridized carbon materials, it

is urgently essential to identify active sites of nitrogen-doped _sp_2-hybridized carbon materials and to understand their interactions with the involved substitute molecules towards

specific reactions. Generally, there are four main types of structural nitrogen configurations including pyrrolic nitrogen (N-5), pyridinic nitrogen (N-6), quaternary or graphitic nitrogen

(N-Q), and oxidized pyridinic nitrogen atoms (N-X) in nitrogen-doped carbon materials. Apart from N-X, one or more of three other nitrogen centers could be considered to be possible

electrochemically active sites28,36,37,38,39,40. However, the inevitable nitrogen configuration mixing in carbon materials, greatly limits the precise identification of active nitrogen

configurations, the fundamental understanding of their mechanisms for specific reactions, and the further development of high-performance nitrogen-doped carbon materials for energy storage

and conversion applications37,41. Engineering single nitrogen configuration-doped carbon materials could ideally tackle this problem. Unfortunately, it seems to be an impossible mission to

engineer single nitrogen configuration-doped carbon materials due to the inevitable thermal treatment involved in synthesizing almost all the nitrogen-doped carbon materials via primarily

either post-synthetic or in situ-doping methods21,25. The post-synthetic doping method mainly involves the thermal treatment of as-synthesized carbon materials with nitrogen-enriched

molecules, including ammonia, urea, melamine, and so on24,42,43. The inhomogeneous and uncontrolled integration of different nitrogen configurations into carbon materials always occurs in

post-synthetic doping processes39. In the in situ doping processes achieved mainly by pyrolysis of nitrogen-enriched carbon precursors, such as small molecules, polymers, and

biomass27,40,44,45,46,47, thermal treatment above ~600 °C always results in a substantial nitrogen loss and induces uncontrollable conversion among different nitrogen configurations48,49;

thermal treatment below ~600 °C always yields lowly graphitized nitrogen-doped carbon materials with poor electrical conductivity50, thereby suppressing their electrochemical activities.

Until now, there have been few reports on single or high-purity pyridinic nitrogen-doped37,51,52 and graphitic nitrogen-doped carbon materials37 and no reports on single pyrrolic

nitrogen-doped carbon materials. Therefore, it is extremely desirable to construct single nitrogen configuration-doped carbon materials, especially pyrrolic nitrogen-doped carbon materials.

Here, we report the preparation of one kind of single nitrogen configuration-doped carbon materials, single pyrrolic N-doped carbon materials (SPNCMs), which are ideal model materials, based

on a facile engineering process that combines the low-temperature dehalogenation induced and alkaline-activated pyrolysis of 3-halogenated phenol-3-aminophenol-formaldehyde (X-APF, X = F,

Cl, and Br) co-condensed resins; the pyrolyzed dehalogenation-induced coupling reaction occurring between adjacent benzene rings promotes enough graphitization of carbon materials at low

temperature, and subsequent alkaline-activated pyrolysis induces the exclusive and complete transformation of _sp_3-hydrided nitrogen species into _sp_2-hydrided pyrrolic nitrogen species.

The pyrrolic nitrogen content of SPNCMs could be rationally tuned from 0 to 4.22 at.% by alternating the molar ratio of 3-aminophenol to 3-fluorophenol, and the final N-doped carbon

materials also exhibit a similar single pyrrolic N-doping state, which was achieved by using 3-chlorophenol or 3-bromophenol as an alternative to 3-fluorophenol. N-doped carbon materials

derived from a 3-aminophenol-FPF co-condensed resin with a 3-aminophenol/3-fluorophenol mole ratio of 1/1, namely SPNCMs (F, 1/1), and with up to 4.22 at.% pyrrolic nitrogen, exhibit a high

specific capacitance of up to 618 F g−1 at 1 A g−1, an outstanding rate performance, and an ultrastable cyclic performance, in which the initial specific capacitance was 467 F g−1 at 10 A 

g−1, and almost 100% of the capacitance was retained over 30,000 cycles performed with a three-electrode system in 1 M H2SO4. More importantly, it could be reliably inferred that pyrrolic

nitrogen species are highly active pseudocapacitive sites for nitrogen-doped carbon materials used as electrochemical capacitive materials. The pseudocapacitance of carbon materials is

positively dependent on the pyrrolic nitrogen content, as shown by the electrochemical analysis of our single pyrrolic nitrogen-doped carbon materials and nitrogen-absent carbon materials

derived from the 3-fluorophenol resin (CMs (FPF)) samples used as ideal model materials, which exhibit both a similar ion diffusion capacity and electrical conductivity. This work presents

an ideal model to fundamentally understand the mechanisms of pyrrolic nitrogen species in N-doped carbon materials for energy storage and conversion applications, thus offering a method for

designing carbon materials doped with tunable structural nitrogen species for different energy conversion applications. RESULTS DESIGN PRINCIPLE AND SYNTHETIC ROUTE OF SPNCMS Figure 1

illustrates the three-step procedure used to synthesize SPNCMs through the combined low-temperature dehalogenation-induced and KOH-activated pyrolysis of X-APF resins, which is described as

follows: (1) The synthesis of SPNCMs (F, 1/1), as a typical example, starts with hydrothermal co-condensation of 3-aminophenol, 3-fluorophenol, and formaldehyde at a mole ratio of 1:1:5, and

this reaction is catalyzed by ammonia, in which both formaldehyde and ammonia result from hexamethylenetetramine (HMT) decomposition. The synthesis of the resulting crosslinked F-APF (1/1)

resin involves the introduction of methylene, a few –CH2–NH– bridging groups and considerable –CH2–N(CH2OH)– bridging groups between 3-aminophenol and 3-fluorophenol monomers, which is

achieved by both the _ortho-_ and _para-_C–H substitution of phenols and N–H substitution of amino groups with methylol groups and the subsequent elimination of H2O and formaldehyde

molecules. (2) The pyrolysis of the F-APF (1/1) resin at 500 °C to form the corresponding nitrogen-doped carbon materials, NCMs (F, 1/1), which are used as the intermediate for SPNCMs,

induces the elimination of HF between the C–F bond on one fluorophenol moiety and the C–H bond on one adjacent aminophenol moiety to directly connect two adjacent benzene rings. Meanwhile,

all the –CH2–N(CH2OH)– bridging groups between two benzene rings are possibly converted into –CH2–NH– heterocyclic structures by the elimination of formaldehyde or into pyrrolic structures

by the elimination of dimethyl ester. In the step, partial hydroxyl groups are preserved and some hydroxyl groups are converted to carbonyl groups. (3) The further KOH-assisted pyrolysis at

500 °C enables the transformation of almost all the –CH2–NH– heterocyclic structures into pyrrolic structures by the elimination of –CH2– groups, thus generating the final SPNCMs (F, 1/1)

with a large enough graphitization degree. Meanwhile, KOH activation removes some carbon atoms to introduce abundant defects and introduces some hydroxyl and carbonyl groups for final SPNCMs

(F, 1/1). When the initial mole ratio of 3-aminophenol/3-fluorophenol is <1, such as 1/3 and 1/7, and even when 3-fluorophenol is replaced with 3-chlorophenol or 3-bromophenol, all the

final N-doped carbon materials exhibit a similar single pyrrolic N-doping state. STRUCTURE AND NITROGEN SPECIES IDENTIFICATION OF SPNCMS Similar to the Raman spectrum of the NCMs (F, 1/1),

that of the SPNCMs (F, 1/1) (Fig. 2a) shows a broad D-band attributed to the breathing mode of the six-fold rings at 1353 cm−1 and a G-band attributed to the in-plane bond-stretching of C

_sp_2 atoms at 1593 cm−1,which are typical feature of _sp_2-hybridized amorphous carbon materials and are consistent with amorphous carbon in stage 2 transforming from nanocrystalline

graphite into _sp_2 a-C53,54. The X-ray diffraction (XRD) patterns of the NCMs (F, 1/1) and SPNCMs (F, 1/1) (Supplementary Fig. 1a) show broadened (002) and (100) diffraction peaks at

20.8–24.4° and 43.5°, respectively55, further verifying the transition from amorphous F-APF (1/1) resins to amorphous NCMs (F, 1/1) and to amorphous SPNCMs (F, 1/1) with a turbostratic

structure. Compared with that of the NCMs (F, 1/1), the pattern of the SPNCMs (F, 1/1) shows that the (002) π-stacking peak shifts to a higher angle and the basal (100) plane is unchanged,

indicating the shortened interplanar distance of the turbostratic structure and, in turn, the KOH-enhanced graphitization-like phenomenon for SPNCMs (F, 1/1)56. However, the interplanar

spacing of the (002) planes of the small nanocrystalline graphite of SPNCMs (F, 1/1) was calculated to be 0.3645 nm, which is far larger than 0.3354 nm, the interplanar spacing of the (002)

plane of ideal graphite. The results indicate the long-range disorder and local short-range order structure of the SPNCMs (F, 1/1), whose structure is consistent with the disordered

structure comprising randomly stacked _sp_2 clusters of the relatively small size, according to the scanning electron microscopy (SEM) (Supplementary Fig. 1b), transmission electron

microscopy (TEM) (Supplementary Fig. 1c), and high-resolution transmission electron microscopy (HRTEM) (Supplementary Fig. 1d) images of the SPNCMs (F, 1/1). Raman and XRD results mentioned

above also exhibit the existence of abundant defects in SPNCMs (F, 1/1). Additionally, energy-dispersive X-ray spectroscopy (EDS) analysis shows uniform doping of nitrogen species into the

turbostratic carbon framework for the SPNCMs (F, 1/1) (Supplementary Fig. 1e–g). As revealed in Supplementary Fig. 2, the Fourier transform infrared (FTIR) spectra provide some useful

information about the structural transformation from the co-condensation resin precursor to the final SPNCMs. The discussion on FTIR spectra is seen in Supplementary Note 1. Furthermore,

X-ray photoelectron spectroscopy (XPS) analysis was used to determine the origin of the single pyrrolic nitrogen configuration in the SPNCMs. Compared with the spectrum of the F-APF (1/1)

resin, the survey spectra of the NCMs (F, 1/1) and SPNCMs (F, 1/1) preserve similar C1_s_, N1_s_, and O1_s_ peaks, and the F signal almost completely disappears (Fig. 2b), indicating

low-temperature defluorination through HF elimination in the first pyrolysis step. The SPNCMs (F, 1/1) preserve the initial N content of the F-APF (1/1) resin (4.27 at.%), with a mere

alternation of the nitrogen configuration via the first pyrolysis step and subsequent KOH activation, according to the high-resolution N 1_s_ XPS spectra of the F-APF(1/1) resin (Fig. 2c),

NCMs (F, 1/1) (Fig. 2d) and SPNCMs (F, 1/1) (Fig. 2e), and full width at half maximum (FWHM) of corresponding deconvoluted peaks (Supplementary Table 1). The N 1_s_ spectrum of the F-APF

(1/1) resin reveals a single peak at 399.25 eV, which corresponds to mixed –CH2–N(CH2OH)– and –CH2–NH– bridging groups; these mixed bridging groups exist because the insufficient

formaldehyde molecules that decomposed from hexamethyl tetraamine could not completely substitute for the hydrogens of the primary amine to generate the –CH2–N(CH2OH)– tertiary amine since

the number of formaldehyde molecules is lower than that of the available active sites, including the primary amine and _ortho_- and _para_-C–H substitution of phenols. The N 1_s_ XPS

spectrum of the NCMs (F, 1/1) intermediate shows the incorporation of a secondary amine (398.9 eV) and N-5 (400.3 eV), which occurs due to the sufficient conversion of the tertiary amine

into a secondary amine and N-5 groups by the elimination of formaldehyde and dimethyl ester, respectively. Importantly, the SPNCMs (F, 1/1) merely contain a single pyrrolic nitrogen

configuration (400.25 eV). X-ray absorption fine structure (XAFS) analysis of N K edge (Fig. 2f) was conducted to further probe the nitrogen structure of the SPNCMs (F, 1/1). In addition to

the 1_s_ → σ* absorption band at 410 eV, there are three well-resolved peaks belonging to 1_s_ → π* features, which range from 400 to 405 eV. The dominant peak at 400.5 eV, namely N-5, is

far stronger than the peaks at 402.4 and 404.2 eV, which are assigned to N-Q (valley-N) and N-X, respectively57, confirming the almost single pyrrolic nitrogen configuration in the SPNCMs

(F, 1/1). Unfortunately, according to XPS analysis, pyridonic nitrogen has a binding energy similar to that of pyrrolic nitrogen, making it difficult to distinguish these two nitrogen

configurations. According to previous reports48,49,58, the two tautomers, 2-hydroxypyridine and α-pyridone, are in equilibrium with one another in pyridonic nitrogen-doped carbon materials.

2-Hydroxypyridine has a chemical environment similar to that of pyridine. Here, 2-hydroxypyridine-type nitrogen has a N 1_s_ binding energy similar to that of pyridine-type nitrogen. Similar

with the nitrogen atom of pyrrole, that of α-pyridone provides two _p_-electrons to the conjugated system, and α-pyridone has a chemical environment similar to that of pyrrole. Therefore,

α-pyridone has an N 1_s_ binding energy similar to that of pyrrolic nitrogen. It is reasonable that the coexistence of 2-hydroxypyridine and α-pyridone in pyridonic nitrogen-doped carbon

materials means that the N 1_s_ XPS spectrum of pyridonic nitrogen could be deconvoluted into two peaks at ~400.4 and 398.9 eV, which are generally assigned to pyrrolic nitrogen and

pyridinic nitrogen. Therefore, we could conclude that the single nitrogen configuration of the binding energy at ~400.3 eV for our nitrogen-doped carbon materials is not pyridone. The

previously reported N 1_s_ spectra of nitrogen-doped carbon materials contains mixed nitrogen configurations at ~400.4 and 398.9 eV, which means that the accurate assignment of pyrrolic

nitrogen and pyridonic nitrogen is extremely difficult for these nitrogen-doped carbon materials. Furthermore, to clarify our single nitrogen configuration as pyrrolic nitrogen or pyridonic

nitrogen, a 3-fluorophenol-2-hyrdoxypyridine-formaldehyde resin, namely F-HPF (F, 1/1), was designed and synthesized through a procedure similar to that used to prepare the

3-fluorophenol-3-aminophenol-formaldehyde resin, F-APF (1/1), in our manuscript. There are no changes in the pyridine and adjacent hydroxyl groups during polymerization of the

phenol-formaldehyde-like resin. In addition, there are no pure pyrrole nor pyridine groups in the F-HPF (1/1) resin. Therefore, the F-HPF (1/1) resin with only pyridone groups could be used

as a model polymer to investigate the pyridone group. Therefore, the FTIR and XPS spectra of the F-HPF (1/1) resin were performed. The FTIR spectrum of the F-HPF (F, 1/1) resin

(Supplementary Fig. 3a) shows obvious vibrations of carbonyl group at 1651 cm−1 and aromatic C=C group at 1622 cm−1, revealing the existence of α-pyridone. The survey spectrum of the F-HPF

(F, 1/1) resin (Supplementary Fig. 3b) shows the coexistence of four elements, including carbon, nitrogen, oxygen, and fluorine. 2-hydroxypyridine and α-pyridone could exist in pyridonic

nitrogen-doped carbon materials (Supplementary Fig. 3b inset). As expected, the N 1_s_ XPS spectrum of F-HPF (F, 1/1) (Supplementary Fig. 3c, d and Supplementary Table 2) could be

deconvoluted into two peaks at 400.35 and 398.95 eV, which are assigned to α-pyridone and 2-hydroxypyridine groups, respectively, and are consistent with the N 1_s_ XPS spectrum of F-HPF (F,

1/1) with the carbonyl group of α-pyridone (531.3 eV) and the hydroxy group of 2-hydroxypyridine (532.95 eV). As mentioned above, we could reliably conclude that the single nitrogen

configuration corresponding to the binding energy at ~400.4 eV for our nitrogen-doped carbon materials is not a pyridone group but is actually a pyrrolic nitrogen configuration. To further

determine the dependence of the nitrogen configuration in the final NCMs on the initial mole ratio of 3-aminophenol/3-fluorophenol, the final NCMs with ratios of 1/0, 3/1, 1/3 and 1/7 were

also synthesized. When the 3-aminophenol/3-fluorophenol ratio increases to higher than 1, the NCMs (APF) exhibit a single nitrogen configuration, which is a possible pyrrolic nitrogen

configuration (400 eV) (Supplementary Fig. 4a and Supplementary Table 3). However, NCMs (APF) used as electrode materials have a poor capacitive behavior, irregular cyclic voltammetry (CV)

curves (Supplementary Fig. 4b) and a potential drop of up to 0.5 V in the potential window of 1 V, as shown in the galvanostatic charge/discharge (GCD) curve obtained at a current density of

0.5 A g−1 (Supplementary Fig. 4c). These results mean that NCMs (APF) with poor electrical conductivity are not suitable for electrochemical applications, which is possibly attributed to

the fact that it is difficult to eliminate hydrogen to couple adjacent benzene rings in the first pyrolysis step. The N 1_s_ XPS spectrum of NCMs (F, 3/1) (Supplementary Fig. 4d and

Supplementary Table 3) exhibit one peak at 401.7 eV, which possibly corresponds to N-Q. As the ratio decreases from 1/1 to 1/3 and to 1/7, dehalogenation-induced and subsequent KOH-activated

pyrolysis ensures the conversion of all the initial nitrogen species into a single pyrrolic nitrogen configuration for the final nitrogen-doped carbon materials, including the SPNCMs (F,

1/1) (Fig. 2e), SPNCMs (F, 1/3) (Fig. 3d), and SPNCMs (F, 1/7) (Fig. 3h) (Supplementary Fig. 5 and Supplementary Table 1) that are attributed to the elimination of sufficient HF molecules

between adjacent benzene rings to form pyrrolic rings, and their corresponding N-5 content decreases from 4.22 to 2.96 and to 1.51 at.%. According to the XPS survey and high-resolution

spectra (Fig. 3i–p, and Supplementary Table 1), when 3-fluorophenol is replaced with 3-chlorophenol or 3-bromophenol, the final nitrogen-doped carbon materials, including SPNCMs (Cl) and

SPNCMs (Br) also exhibit similar single pyrrolic nitrogen-doping states. Hence, it could be deduced that the two-step pyrolysis of the X-APF co-condensed resin is a reliable and general

strategy to engineer SPNCMs. In addition to a single pyrrolic nitrogen-configuration, oxygen species with high contents were found in all our SPNCMs, which is mainly ascribed to KOH

activation. The high-resolution O 1_s_ XPS spectra of SPNCMs (F, 1/1), SPNCMs (F, 1/3), and SPNCMs (F, 1/7) are shown in Supplementary Fig. 6a–c and Supplementary Table 4. The O 1_s_ XPS

spectra of all three of these carbon materials reveal the presence of a hydroxyl/etheric group due to the peak with a binding energy of 533.1–533.3 eV and a carbonyl group due to the peak

with a binding energy of 531.9–532.2 eV. ION TRANSFER AND ELECTRON-CONDUCTIVE CAPACITIES OF SPNCMS It can be generally accepted that N-5 and N-6 are assumed to be related to the Faradaic

redox reactions-dependent pseudocapacitance of nitrogen-doped carbon materials59,60. However, inevitable nitrogen configuration mixing hampers the ability to distinguish the contribution of

N-5 and N-6 pseudocapacitance. Using SPNCMs with different N-5 contents as model carbon materials presents an opportunity to clarify the pyrrolic nitrogen-dependent pseudocapacitance for

nitrogen-doped carbon materials. According to Fig. 4, the N-5 redox reaction involving the transfer of both a proton and an electron61, a similar ion transfer capacity and electronic

conductivity as well as a single pyrrolic nitrogen configuration are also crucial to precisely elucidate the N-5 pseudocapacitance contribution to carbon materials. Due to an inevitable

oxygen residue in carbon materials upon their KOH activation62, nitrogen-absent CMs (FPF) derived from the combined low-temperature dehalogenation-induced and alkaline-activated pyrolysis of

a 3-fluorophenol-formaldehyde (FPF) resin were chosen as the control sample to exclude the contribution of oxygen pseudocapacitance to our SPNCMs. The N2 adsorption/desorption isotherms of

the SPNCMs (F, 1/1), SPNCMs (F, 1/3), SPNCMs (F, 1/7), and CMs (FPF) (Supplementary Fig. 7a) reveal similar type I isotherm features typical of a microporous structure, according to the

IUPAC classification, and these four carbon materials have uniform slit micropore geometries at ~0.5–0.7 nm (Supplementary Fig. 7b–d), which means they exhibit similar electrolyte ion

transfer capacities. These four carbon materials also show similar excellent electronic conductivity, as inferred from their low equivalent series resistances ~0.74, 0.75, 0.79, and 0.80 Ω

for the SPNCMs (F, 1/1), SPNCMs (F, 1/3), SPNCMs (F, 1/7), and CMs (FPF), respectively, which correspond to the _x_-intercepts in the Nyquist plots obtained through electrochemical impedance

spectroscopy (EIS) (Supplementary Fig. 8 and Supplementary Fig. 8 inset). All these nearly vertical curves in the low-frequency region indicate excellent capacitive behaviors. As shown in

Fig. 2a and Supplementary Fig. 9, the Raman spectra of the SPNCMs (F, 1/1), SPNCMs (F, 1/3), SPNCMs (F, 1/7), and CMs (FPF) have features similar to those of _sp_2-hybridized amorphous

carbon materials, with a broad D-band and G-band. PYRROLIC NITROGEN CONTENT-DEPENDENT PSEUDOCAPACITANCE Accordingly, these four types of carbon materials could be used as model materials to

evaluate the N-5-depenent electrocapacitive performance. All the CV curves obtained at 1 mV s−1 consist of one nearly rectangular curve, indicating an electrical double layer capacitance

(EDLC) behavior and a couple of symmetric peaks at 0.3–0.4 V, derived from the reversible Faradaic redox reactions of N-5 species and/or oxygen (Fig. 5a). Meanwhile, all the symmetric GCD

curves (Fig. 5b) at 1 A g−1 with obviously distorted linear shapes also indicate typical pseudocapacitive behaviors. As the N-5 content in different carbon materials, ranging from

nitrogen-absent CMs (FPF) to SPNCMs (F, 1/7), SPNCMs (F, 1/3), and SPNCMs (F, 1/1) increases, their total specific capacitances increase according to the corresponding CV (Fig. 5a) or GCD

(Fig. 5b) curves. All the electrochemical measurements of these carbon materials, ranging from 1 to 20 mV s−1 and from 1 to 20 A g−1, preserve similar CV (Supplementary Fig. 10a–e) and GCD

curves (Supplementary Fig. 11a–e), with a combined EDLC and pseudocapacitance, respectively, and show an outstanding rate performance and slightly decreased capacitances. Particularly, the

SPNCMs (F, 1/1) with the highest N-5 content show a specific capacitance of up to 618 F g−1 at 1 A g−1 and maintain a high specific capacitance of 447 F g−1, even up to 20 A g−1. In

addition, the SPNCMs (F, 1/1) both maintain a high specific capacitance of 467 F g−1 up to 10 A g−1 and reveal an ultrahigh stability over 30,000 cycles (Supplementary Fig. 12a, b). To

confirm the electrochemical stability of the SPNCMs (F, 1/1), SEM, TEM, HRTEM, and XPS analyses of the recovered SPNCMs (F,1/1) electrode material were conducted after GCD testing over

30,000 cycles. The SEM (Supplementary Fig. 12c) and TEM (Supplementary Fig. 12d) images demonstrate that the recovered SPNCMs (F,1/1) electrode material maintains the initial morphologic

feature of randomly assembled layers. As observed in the HRTEM image (Supplementary Fig. 12e), the recovered SPNCMs (F,1/1) electrode material exhibits a turbostratic carbon structure

similar to that of the fresh SPNCMs (F,1/1). EDS analysis (Supplementary Fig. 12f–h) confirms that the recovered SPNCMs (F, 1/1) electrode material maintains the uniform doping of nitrogen

species into the turbostratic carbon framework. Furthermore, XPS analysis (Supplementary Fig. 12i, j, and Supplementary Table 5) reveals that the recovered SPNCMs (F,1/1) electrode material

maintains a nitrogen content (4.8 at.%) similar to that of the fresh SPNCMs (F,1/1) (4.22 at.%). Unlike the single pyrrolic nitrogen configuration of the fresh SPNCMs (F,1/1) (Fig. 2e), the

N 1_s_ XPS spectrum of the recovered SPNCMs (F,1/1) electrode material (Supplementary Fig. 12i) shows the coexistence of pyrrolic nitrogen at 400.4 eV and oxidized pyrrolic nitrogen at 401.9

 eV, which could be ascribed to the fact that a redox reaction of pyrrolic nitrogen/electrochemically oxidized pyrrolic nitrogen occurs upon charging–discharging cycles, and the rapid

charging–discharging cycles at 10 A g−1 of the large current density possibly results in the incomplete use of pyrrolic nitrogen and incomplete reduction of electrochemically oxidized

pyrrolic nitrogen. The O 1_s_ XPS spectrum of the recovered SPNCMs (F,1/1) electrode material (Supplementary Fig. 12j) still shows the coexistence of a hydroxyl/etheric group due to the peak

with a binding energy of 533.3 eV and a carbonyl group due to the peak with a binding energy of 532 eV, which is similar to the O 1_s_ XPS spectrum of the fresh SPNCMs (F,1/1) material. The

above-mentioned results confirm the high stability of the SPNCMs (F,1/1) electrode material. Generally, N-doped carbon materials exhibit a combined EDLC and faradaic pseudocapacitance and

their EDLCs can be quantitatively identified though electrochemical surface area (ESA) tests performed in the nonFaradaic voltage range63,64. To further explore the N-5 pseudocapacitive

contribution, based on these nearly rectangular CV curves (Supplementary Fig. 13a–d) ranging from 0 to 0.05 V vs. SCE and the slopes of the scan rate-dependent current density curves

(Supplementary Fig. 13e), the EDLCs of the SPNCMs (F, 1/1), SPNCMs (F, 1/3), SPNCMs (F, 1/7), and CMs(FPF) were firstly calculated though ESA tests to be ~125, 263, 211, and 183 F g−1,

respectively, which are highly consistent with their corresponding specific surface areas (SSA) of 450, 950, 873, and 880 cm2 g−1, respectively. Generally, KOH activation generates

nanopores, leading to an increase in defect density for carbon materials. Up to date, it is extremely difficult to precisely control and determine the defect type and density of defects for

carbon materials due to the limitations of present characterization. Fortunately, specific surface area represents the density of nanopore-dependent defects for our final carbon materials to

a large content. Therefore, the capacitance from these defects could be approximately regarded as the double layer capacitance. Based on their EDLCs and total specific capacitance of 584.8,

486.7, 412.4, and 301.5 F g−1 at 1 mV s−1, the corresponding faradaic pseudocapacitances of the SPNCMs (F, 1/1), SPNCMs (F, 1/3), SPNCMs (F, 1/7), and CMs (FPF) can be calculated as 459.8,

223.7, 201.4, and 118.5 F g−1, respectively. Similar to the SPNCMs, the nitrogen-absent carbon material, CMs (FPF), show a typical pseudocapacitive characteristic, with symmetric redox peaks

at 0.3–0.4 V vs. SCE, as observed from the CV measurement performed at different scan rates (Supplementary Fig. 10d), demonstrating the reversible Faradaic redox reactions of oxygen species

possibly derived from the quinone/hydroquinone redox reaction, which is consistent with a couple of symmetric redox peaks at ~0.4 V vs. SCE for surface-oxidized carbon nanotubes65 and

electrochemically modified glassy carbon66. The quinone/hydroquinone redox reaction was described in Fig. 6. The high-resolution O 1_s_ XPS spectrum of the CMs (FPF) (Supplementary Fig. 6d)

reveals the presence of a hydroxyl/etheric group due to the peak with a binding energy of 533.3 eV and a carbonyl group due to the peak with a binding energy of 532.1 eV, and these peaks are

similar to those observed in the O 1_s_ XPS spectra of SPNCMs (F, 1/1), SPNCMs (F, 1/3), and SPNCMs (F, 1/7) (Supplementary Fig. 6a–c). A couple of carbonyl groups could behave as quinones,

and a couple of hydroxyl groups behave as hydroquinones. These results mean that these pseudocapacitances of high-oxygen-content SPNCMs (F,1/1, F, 1/3, and F 1/7) with structures similar to

those of nitrogen-absent CMs (FPF) could partially derive from the quinone/hydroquinone redox reaction. So far, due to the great difficulty in precisely determining the structure and number

of electrochemically active oxygen species and difficulty in excluding electrochemically inert oxygen species for carbon materials, the merely oxygen-dependent pseudocapacitance of CMs

(FPF) exhibiting symmetric redox peaks in their CV measurements performed at different scan rates (Supplementary Fig. 10d) has to be assumed to derive from all the oxygen atoms with

identical pseudocapacitive contributions. Considering the pseudocapacitance of 118.5 F g−1 for CMs (FPF) and the oxygen content determined by the XPS analysis (Supplementary Table 6), the

specific pseudocapacitance per mole of oxygen atoms can be calculated to be 8471.75 F. Accordingly, the oxygen-dependent specific pseudocapacitances were calculated to be 105.9, 100.8, and

146.3 F g−1 for the SPNCMs (F, 1/1), SPNCMs (F, 1/3), and SPNCMs (F, 1/7), respectively, and then, their corresponding single pyrrolic nitrogen-dependent pseudocapacitances were calculated

to be 353.9, 122.9, 55.1 F g−1, respectively (Supplementary Table 7, Fig. 7). Therefore, it could be deduced that the pseudocapacitance is positively dependent on the N-5 content in

nitrogen-doped carbon materials because of our SPNCMs, which exhibit a similar ion diffusion capacity, electron conductivity and single pyrrolic nitrogen configuration. To further determine

whether pyrrolic nitrogen is suitable as an electrochemically active site for Faradic reactions, the SPNCMs (F, 1/1) after charging and discharging at a current density of 1 A g−1 in a 1.0 M

H2SO4 solution were recovered to investigate the electrochemical redox change of the SPNCMs (F, 1/1). The nitrogen content of the fresh SPNCMs (F, 1/1), the recovered SPNCMs (F, 1/1) after

charging, and the recovered SPNCMs (F, 1/1) after discharging is 4.22, 3.97 and 3.69 at.%, respectively, based on XPS analysis, which means that there is no obvious change in the nitrogen

content for SPNCMs (F, 1/1) before and after performing GCD tests. The high-resolution N 1_s_ spectra of these three samples (Fig. 2e, Supplementary Table 1, Supplementary Fig. 14a, 14b, and

Supplementary Table 8) show the dramatic conversion of pyrrolic nitrogen (~400.2 eV) into oxidized pyrrolic nitrogen (~401.9 eV) after charging and the corresponding obvious reverse

conversion process after discharging, which confirms that pyrrolic nitrogen is an electrochemically active site for nitrogen-doped carbon materials exhibiting pseudocapacitance. Meanwhile,

the oxygen content of the fresh SPNCMs (F, 1/1), the recovered SPNCMs (F, 1/1) after charging, and the recovered SPNCMs (F, 1/1) after discharging is 16.69, 18.64, and 15.45 at.%,

respectively, based on XPS analysis, which means that there is no obvious change in the oxygen content for SPNCMs (F, 1/1) before and after performing GCD tests. The high-resolution O 1_s_

spectra of these three samples (Supplementary Fig. 6a, Supplementary Table 4, Supplementary Fig. 14c, 14d, and Supplementary Table 8) show the conversion of a hydroxyl group (~533.3 eV) into

a carbonyl group (~532.1 eV) after charging and the corresponding partial reverse conversion after discharging, which is possibly ascribed to quinone/hydroquinone redox reaction. DISCUSSION

In summary, we report SPNCMs with tunable nitrogen contents used as model nitrogen-doped carbon materials and prepared though two-step pyrolysis of X-APF co-condensed resins. Moreover, it

could be inferred that N-5 species are highly active pseudocapacitive sites for nitrogen-doped carbon materials, which was inferred based on the result that the pseudocapacitance of the

carbon materials is positively dependent on the N-5 content, as shown by the electrochemical analyses of the SPNCMs and nitrogen-absent CMs (FPF). The discovery of SPNCMs as ideal model

carbon materials not only identifies N-5 species as active sites and their mechanisms toward energy storage and conversion applications, but also offers a method for designing carbon

materials doped with tunable structural nitrogen species for different energy conversion applications. METHODS MATERIALS 3-Aminophenol (3-AP; >98.5%), HMT (99.5%), and 3-Bromophenol (98%)

were purchased from TCI, Alfa-Aesar, and Aladdin Industrial Corporation, respectively. 3-Fluorophenol (98%), 3-Chlorophenol (98%), and potassium hydroxide (KOH; GR; 95%) were purchased from

Shanghai Macklin Biochemical Co., Ltd. Sulfuric acid and hydrochloric acid were supplied by Tianjin Kermel Chemical Reagent Co., and polyvinylidene difluoride (PVDF) was obtained from

Guangdong Candlelight Amperex Technology Ltd. MATERIALS PREPARATION Supplementary Tables 9–11 show the details of the synthesis parameters of the 3-halogenated

phenol-3-aminophenol-formaldehyde (X-APF) co-condensed resin (X = F, Cl, and Br), the corresponding pyrolyzed intermediates and the final nitrogen-doped carbon materials after activation.

Typically, certain amounts of 3-aminophenol, 3-fluorinephenol (3-chlorophenol or 3-bromophenol), and HMT were mixed in 80 ml deionized water, stirred for 1 h at room temperature, and then

transferred into a Teflon-lined stainless-steel autoclave, followed by heating at 160 °C for 4 h. The brown product was purified with distilled water several times through a suction device

and then dried at 60 °C for 12 h. Subsequently, the first pyrolysis step was applied to the corresponding cocondensed resins were conducted. The as-obtained materials were placed into a tube

furnace, heated to 500 °C with a ramp rate of 1 °C min−1 and then held for 4 h under pure nitrogen gas (99.999%) at a flow rate of 200 mL/min. Finally, the mixture of the above-mentioned

pyrolyzed product and KOH was heated at 500 °C for 8 h until the whole mixture turned into a paste, followed by washing with an HCl solution and deionized water. After being dried, the final

product after activation was obtained. The 3-Fluorophenol-2-hyrdoxypyridine-formaldehyde resin, namely, F-HPF (F, 1/1), was designed and synthesized through the following procedure: 0.085 g

of 2-hydroxypyridine, 0.1 g of 3-fluorinephenol, and 0.074 g of HMT were mixed in 80 ml deionized water, stirred for 1 h at room temperature, and then transferred into a Teflon-lined

stainless-steel autoclave, followed by heating at 180 °C for 24 h. The product was purified with distilled water several times through a suction device and then dried at 60 °C for 12 h.

CHARACTERIZATION The structures of the samples were characterized on a HITACHI HT 7700 transmission electron microscope, with an accelerating voltage of 100 kV. HRTEM and EDS analyses were

performed on a JEM-2010 instrument operated at an accelerating voltage of 200 kV. SEM images were acquired on a SUPRA 55 field-emission scanning electron microscope with an accelerating

voltage of 200 kV. The powder XRD data was conducted on a RIGAKU X-ray diffractometer with CuKa radiation (_l_ = 0.15418 nm) at 40 kV and calibrated using the RIGAKU Silicon-640 as standard

sample before the measurement. Raman spectra were recorded on a Renishaw in Via Raman microscope with an Ar ion laser at the excitation wavelength of 532 nm. XPS analyses were performed with

an ESCALAB 250 Xi spectrometer by employing an Al Kα X-ray source. The pass energies for XPS survey spectra and high-resolution XPS spectra test of all the samples are 100.0 and 30.0 eV,

respectively. All the high-resolution XPS spectra were fitted with the Lorentz/Gauss mixing ratios fixed at 0.8, sample charging was corrected by using the C 1_s_ binding energy at 284.8 eV,

and Shirley-type background subtraction was applied. As listed in Supplementary Tables 1–5, 8, the FWHMs of N 1_s_ were determined to be 1.9–2 eV, and the FWHMs of O 1_s_ are determined to

be ~1.8 eV. FTIR spectra were recorded on a Nicolet IS 10 infrared spectrometer. N K edge XAFS spectrum of the SPNCMs (F, 1/1) was tested in the total electron yield (TEY) mode by BSRF 4B7B.

ELECTROCHEMICAL MEASUREMENT The working electrodes were prepared by pressing the mixture of samples, acetylene carbon black, and PVDF binder at the mass ratio of 85/10/5 in 1 M H2SO4. The

above mixture ~1 mg cm−2) was coated onto a 1 × 1 cm platinum net and dried at 120 °C for 12 h in vacuum. Electrochemical performance of supercapacitor was firstly tested in a

three-electrode system in 1 M H2SO4. The platinum foil and Hg/Hg2Cl2 (SCE) in 1 M H2SO4 were used as counter electrode and reference electrode, respectively. EIS spectra were recorded at the

frequency range of 0.01–105 Hz. CV curves were measured at the scanning rate of 1–20 mV s−1. Both EIS and CV tests were carried out on a CHI 660E electrochemical workstation. The constant

current charge–discharge tests were performed with a computer-controlled cycling equipment (Land CT2001A, China) in the potential rage of −0.15 to 0.85 V vs. SCE in 1 M H2SO4. CALCULATION

EQUATIONS FOR SUPERCAPACITOR The capacitance calculation of three electrode system according to Eq. (1) with the formula: $$C = \frac{{S_{{\mathrm{{Area}}}}}}{{2\nu {\Delta}V}}$$ (1) where

\(S_{{\mathrm{{Area}}}} = {\oint} I{\mathrm{{d}}}V\) is the loop area from the CV test; \(\nu\) is the scan rate; and \({\Delta}V\) on behalf of the potential window within one cycle. The

specific capacitance was estimated from the galvanostatic charge–discharge curves, by Eq. (2): $$C_{\mathrm{{S}}} = \frac{{I \times {\Delta}t}}{{m \times {\Delta}V}}$$ (2) where _I_,

\({\Delta}t\), _m_, and \({\Delta}V\) stand for the discharge current, discharge time, the total mass of active material on three electrodes. The EDLC capacitance was determined by

electrochemical surface areas (ESA) in the non-Faradic voltage range, by Eqs. (3) and (4): $${\mathrm{ESA}} = \frac{{I_1 - I_2}}{{\nu _1 - \nu _2}}$$ (3) $$C_{{\mathrm{{EDLC}}}} =

\frac{{{\mathrm{ESA}}}}{M}$$ (4) where \(I\) is the current density; \(\nu\) is the scan rate; and _M_ is the mass of active material per unit area. DATA AVAILABILITY The data that support

the findings of this study are available from the corresponding author upon reasonable request. Source data are provided with this paper. REFERENCES * Banerjee, A. et al. Ultralarge elastic

deformation of nanoscale diamond. _Science_ 360, 300–302 (2018). Article  CAS  PubMed  Google Scholar  * Mochalin, V. N., Shenderova, O., Ho, D. & Gogotsi, Y. The properties and

applications of nanodiamonds. _Nat. Nanotechnol._ 7, 11–23 (2012). Article  ADS  CAS  Google Scholar  * Prasher, R. Graphene spreads the heat. _Science_ 328, 185–186 (2010). Article  CAS 

PubMed  Google Scholar  * Balandin, A. A. Thermal properties of graphene and nanostructured carbon materials. _Nat. Mater._ 10, 569–581 (2011). Article  ADS  CAS  PubMed  Google Scholar  *

Hone, J. et al. Electrical and thermal transport properties of magnetically aligned single wall carbon nanotube films. _Appl. Phys. Lett._ 77, 666–668 (2000). Article  ADS  CAS  Google

Scholar  * Berger, C. et al. Electronic confinement and coherence in patterned epitaxial graphene. _Science_ 312, 1191–1195 (2006). Article  ADS  CAS  PubMed  Google Scholar  * Li, Y., Xu,

L., Liu, H. & Li, Y. Graphdiyne and graphyne: from theoretical predictions to practical construction. _Chem. Soc. Rev._ 43, 2572–2586 (2014). Article  CAS  PubMed  Google Scholar  *

Huang, C. et al. Progress in research into 2D graphdiyne-based materials. _Chem. Rev._ 118, 7744–7803 (2018). Article  CAS  PubMed  Google Scholar  * Lu, Z. et al. High-efficiency oxygen

reduction to hydrogen peroxide catalysed by oxidized carbon materials. _Nat. Catal._ 1, 156–162 (2018). Article  CAS  Google Scholar  * Duan, X. et al. Metal-free carbon materials for CO2

electrochemical reduction. _Adv. Mater._ 29, 1701784 (2017). Article  CAS  Google Scholar  * Zhao, Y. et al. N–P–O co-doped high performance 3D graphene prepared through red

phosphorous-assisted “cutting-thin” technique: a universal synthesis and multifunctional applications. _Nano Energy_ 28, 346–355 (2016). Article  CAS  Google Scholar  * Liu, J. et al.

Carbon-supported divacancy-anchored platinum single-atom electrocatalysts with superhigh Pt utilization for the oxygen reduction reaction. _Angew. Chem. Int. Ed._ 58, 1163–1167 (2019).

Article  CAS  Google Scholar  * Wang, T. et al. Carbon-rich nonprecious metal single atom electrocatalysts for CO2 reduction and hydrogen evolution. _Small Methods_ 3, 1900210 (2019).

Article  CAS  Google Scholar  * Hui, L. et al. Highly efficient and selective generation of ammonia and hydrogen on a graphdiyne-based catalyst. _J. Am. Chem. Soc._ 141, 10677–10683 (2019).

Article  CAS  PubMed  Google Scholar  * Li, J. et al. Ultrahigh-loading zinc single-atom catalyst for highly efficient oxygen reduction in both acidic and alkaline media. _Angew. Chem. Int.

Ed._ 58, 1–6 (2019). Article  Google Scholar  * Xue, Y. et al. Anchoring zero valence single atoms of nickel and iron on graphdiyne for hydrogen evolution. _Nat. Commun._ 9, 1460 (2018).

Article  ADS  PubMed  PubMed Central  CAS  Google Scholar  * Wood, K. N., O’Hayre, R. & Pylypenko, S. Recent progress on nitrogen/carbon structures designed for use in energy and

sustainability applications. _Energy Environ. Sci._ 7, 1212–1249 (2014). Article  CAS  Google Scholar  * Jiao, Y., Zheng, Y., Jaroniec, M. & Qiao, S. Z. Design of electrocatalysts for

oxygen- and hydrogen-involving energy conversion reactions. _Chem. Soc. Rev._ 44, 2060–2086 (2015). Article  CAS  PubMed  Google Scholar  * Liu, X. & Dai, L. Carbon-based metal-free

catalysts. _Nat. Rev. Mater._ 1, 16064 (2016). Article  ADS  CAS  Google Scholar  * Lin, T. et al. Nitrogen-doped mesoporous carbon of extraordinary capacitance for electrochemical energy

storage. _Science_ 350, 1508–1513 (2015). Article  ADS  CAS  PubMed  Google Scholar  * Wang, Q., Yan, J. & Fan, Z. Carbon materials for high volumetric performance supercapacitors:

design, progress, challenges and opportunities. _Energy Environ. Sci._ 9, 729–762 (2016). Article  CAS  Google Scholar  * Gong, K., Du, F., Xia, Z., Durstock, M. & Dai, L. Nitrogen-doped

carbon nanotube arrays with high electrocatalytic activity for oxygen reduction. _Science_ 323, 760–764 (2009). Article  ADS  CAS  PubMed  Google Scholar  * Behan, J. A. et al. Untangling

cooperative effects of pyridinic and graphitic nitrogen sites at metal-free N-doped carbon electrocatalysts for the oxygen reduction reaction. _Small_ 15, 1902081 (2019). Article  CAS 

Google Scholar  * Lv, Q. et al. Selectively nitrogen-doped carbon materials as superior metal-free catalysts for oxygen reduction. _Nat. Commun._ 9, 3376 (2018). Article  ADS  PubMed  PubMed

Central  CAS  Google Scholar  * Dai, L., Xue, Y., Qu, L., Cho, H.-J. & Baek, J.-B. Metal-free catalysts for oxygen reduction reaction. _Chem. Rev._ 115, 4823–4892 (2015). Article  CAS 

PubMed  Google Scholar  * Zhang, S. et al. Polyethylenimine-enhanced electrocatalytic reduction of CO2 to formate at nitrogen-doped carbon nanomaterials. _J. Am. Chem. Soc._ 136, 7845–7848

(2014). Article  CAS  PubMed  Google Scholar  * Sharma, P. P. et al. Nitrogen‐doped carbon nanotube arrays for high‐efficiency electrochemical reduction of CO2: on the understanding of

defects, defect density, and selectivity. _Angew. Chem. Int. Ed._ 54, 13701–13705 (2015). Article  CAS  Google Scholar  * Cui, X., Pan, Z., Zhang, L., Peng, H. & Zheng, G. Selective

etching of nitrogen-doped carbon by steam for enhanced electrochemical CO2 reduction. _Adv. Energy Mater._ 7, 1701456 (2017). Article  CAS  Google Scholar  * Hu, C. & Dai, L.

Multifunctional carbon-based metal-free electrocatalysts for simultaneous oxygen reduction, oxygen evolution, and hydrogen evolution. _Adv. Mater._ 29, 1604942 (2017). Article  CAS  Google

Scholar  * Sun, J. et al. Ultrathin nitrogen-doped holey carbon@graphene bifunctional electrocatalyst for oxygen reduction and evolution reactions in alkaline and acidic media. _Angew. Chem.

Int. Ed._ 57, 16511–16515 (2018). Article  CAS  Google Scholar  * Jiang, H. et al. Defect-rich and ultrathin N doped carbon nanosheets as advanced trifunctional metal-free electrocatalysts

for the ORR, OER and HER. _Energy Environ. Sci._ 12, 322–333 (2019). Article  CAS  Google Scholar  * Jiao, Y., Zheng, Y., Davey, K. & Qiao, S.-Z. Activity origin and catalyst design

principles for electrocatalytic hydrogen evolution on heteroatom-doped graphene. _Nat. Energy_ 1, 16130 (2016). Article  ADS  CAS  Google Scholar  * Lv, C. et al. Defect engineering

metal-free polymeric carbon nitride electrocatalyst for effective nitrogen fixation under ambient conditions. _Angew. Chem. Int. Ed._ 57, 10246–10250 (2018). Article  CAS  Google Scholar  *

Mukherjee, S. et al. Metal-organic framework-derived nitrogen-doped highly disordered carbon for electrochemical ammonia synthesis using N2 and H2O in alkaline electrolytes. _Nano Energy_

48, 217–226 (2018). Article  CAS  Google Scholar  * Zhao, C. et al. Ambient electrosynthesis of ammonia on a biomass-derived nitrogen-doped porous carbon electrocatalyst: contribution of

pyridinic nitrogen. _ACS Energy Lett._ 4, 377–383 (2019). Article  CAS  Google Scholar  * Wang, H. et al. Efficient electrocatalytic reduction of CO2 by nitrogen-doped nanoporous

carbon/carbon nanotube membranes: a step towards the electrochemical CO2 refinery. _Angew. Chem. Int. Ed._ 56, 7847–7852 (2017). Article  CAS  Google Scholar  * Guo, D. et al. Active sites

of nitrogen-doped carbon materials for oxygen reduction reaction clarified using model catalysts. _Science_ 351, 361–365 (2016). Article  ADS  CAS  PubMed  Google Scholar  * Xing, T. et al.

Observation of active sites for oxygen reduction reaction on nitrogen-doped multilayer graphene. _ACS Nano_ 8, 6856–6862 (2014). Article  CAS  PubMed  Google Scholar  * Lai, L. et al.

Exploration of the active center structure of nitrogen-doped graphene-based catalysts for oxygen reduction reaction. _Energy Environ. Sci._ 5, 7936–7942 (2012). Article  CAS  Google Scholar

  * Liu, S. et al. Identifying active sites of nitrogen‐doped carbon materials for the CO2 reduction reaction. _Adv. Funct. Mater._ 28, 1800499 (2018). Article  CAS  Google Scholar  * Yang,

L. et al. Carbon-based metal-free ORR electrocatalysts for fuel cells: past, present, and future. _Adv. Mater._ 31, 1804799 (2019). Article  CAS  Google Scholar  * Lin, Z., Waller, G., Liu,

Y., Liu, M. & Wong, C.-P. Facile synthesis of nitrogen‐doped graphene via pyrolysis of graphene oxide and urea, and its electrocatalytic activity toward the oxygen–reduction reaction.

_Adv. Energy Mater._ 2, 884–888 (2012). Article  CAS  Google Scholar  * Sheng, Z.-H. et al. Catalyst-free synthesis of nitrogen-doped graphene via thermal annealing graphite oxide with

melamine and its excellent electrocatalysis. _ACS Nano_ 5, 4350–4358 (2011). Article  CAS  PubMed  Google Scholar  * Wang, Z. et al. Nitrogen-promoted self-assembly of N-doped carbon

nanotubes and their intrinsic catalysis for oxygen reduction in fuel cells. _ACS Nano_ 5, 1677–1684 (2011). Article  CAS  PubMed  Google Scholar  * Zhao, Y., Nakamura, R., Kamiya, K.,

Nakanishi, S. & Hashimoto, K. Nitrogen-doped carbon nanomaterials as non-metal electrocatalysts for water oxidation. _Nat. Commun._ 4, 2390 (2013). Article  ADS  PubMed  Google Scholar 

* Chen, L.-F., Lu, Y., Yu, L. & Lou, X. W. Designed formation of hollow particle-based nitrogen-doped carbon nanofibers for high-performance supercapacitors. _Energy Environ. Sci._ 10,

1777–1783 (2017). Article  CAS  Google Scholar  * Yang, T. et al. A sustainable route from biomass byproduct okara to high content nitrogen‐doped carbon sheets for efficient sodium ion

batteries. _Adv. Mater._ 28, 539–545 (2016). Article  CAS  PubMed  Google Scholar  * Pels, J. R., Kapteijn, F., Moulijn, J. A., Zhu, Q. & Thomas, K. M. Evolution of nitrogen

functionalities in carbonaceous materials during pyrolysis. _Carbon_ 33, 1641–1653 (1995). Article  CAS  Google Scholar  * Schmiers, H., Friebel, J., Streubel, P., Hesse, R. & Köpsel, R.

Change of chemical bonding of nitrogen of polymeric N-heterocyclic compounds during pyrolysis. _Carbon_ 37, 1965–1978 (1999). Article  CAS  Google Scholar  * Bucker, W. Preparation and DC

conductivity of an amorphous organic semiconducting system. _J. Non-Cryst. Solids_ 12, 115–128 (1973). Article  ADS  Google Scholar  * Luo, Z. et al. Pyridinic N doped graphene: synthesis,

electronic structure, and electrocatalytic property. _J. Mater. Chem._ 21, 8038–8044 (2011). Article  CAS  Google Scholar  * Sun, M. et al. Tailoring platelet carbon nanofibers for

high-purity Pyridinic-N doping: A novel method for synthesizing oxygen reduction reaction catalysts. _Carbon_ 125, 401–408 (2017). Article  CAS  Google Scholar  * Ferrari, A. &

Robertson, J. Interpretation of Raman spectra of disordered and amorphous carbon. _Phys. Rev. B_ 61, 14095–14107 (2000). Article  ADS  CAS  Google Scholar  * Ferrari, A. & Robertson, J.

Raman spectroscopy of amorphous, nanostructured, diamond-like carbon, and nanodiamond. _Philos. Trans. R. Soc. Lond. A_ 362, 2477–2512 (2004). Article  ADS  CAS  Google Scholar  * Bonino, F.

et al. A disordered carbon as a novel anode material in lithium-ion cells. _Adv. Mater._ 17, 743–746 (2005). Article  CAS  Google Scholar  * Stobinski, L. et al. Graphene oxide and reduced

graphene oxide studied by the XRD, TEM and electron spectroscopy methods. _J. Electron Spectrosc._ 195, 145–154 (2014). Article  CAS  Google Scholar  * Sharifi, T., Hu, G., Jia, X. &

Wågberg, T. Formation of active sites for oxygen reduction reactions by transformation of nitrogen functionalities in nitrogen-doped carbon nanotubes. _ACS Nano_ 6, 8904–8912 (2012). Article

  CAS  PubMed  Google Scholar  * Biemolt, J., Denekamp, I. M., Slot, T. K., Rothenberg, G. & Eisenberg, D. Boosting the supercapacitance of nitrogen-doped carbon by tuning surface

functionalities. _ChemSusChem_ 10, 4018–4024 (2017). Article  CAS  PubMed  PubMed Central  Google Scholar  * Jeong, H. M. et al. Nitrogen-doped graphene for high-performance ultracapacitors

and the importance of nitrogen-doped sites at basal planes. _Nano Lett._ 11, 2472–2477 (2011). Article  ADS  CAS  PubMed  Google Scholar  * Wang, Y., Song, Y. & Xia, Y. Electrochemical

capacitors: mechanism, materials, systems, characterization and applications. _Chem. Soc. Rev._ 45, 5925–5950 (2016). Article  CAS  PubMed  Google Scholar  * Wickramaratne, N. P. et al.

Nitrogen enriched porous carbon spheres: attractive materials for supercapacitor electrodes and CO2 adsorption. _Chem. Mater._ 26, 2820–2828 (2014). Article  CAS  Google Scholar  * Zhu, Y.

et al. Carbon-based supercapacitors produced by activation of graphene. _Science_ 332, 1537–1541 (2011). Article  ADS  CAS  PubMed  Google Scholar  * Augustyn, V. et al. High-rate

electrochemical energy storage through Li+ intercalation pseudocapacitance. _Nat. Mater._ 12, 518–522 (2013). Article  ADS  CAS  PubMed  Google Scholar  * Simon, P., Gogotsi, Y. & Dunn,

B. Where do batteries end and supercapacitors begin? _Science_ 343, 1210–1211 (2014). Article  ADS  CAS  PubMed  Google Scholar  * Li, L. & Xing, Y. Electrochemical durability of carbon

nanotubes in noncatalyzed and catalyzed oxidations. _J. Electrochem. Soc._ 153, A1823–A1828 (2006). Article  CAS  Google Scholar  * Sullivan, M. G. et al. Electrochemically modified glassy

carbon for capacitor electrodes characterization of thick anodic layers by cyclic voltammetry, differential electrochemical mass spectrometry, spectroscopic ellipsometry, X-ray photoelectron

spectroscopy, FTIR, and AFM. _J. Electrochem. Soc._ 147, 2636–2643 (2000). Article  ADS  CAS  Google Scholar  Download references ACKNOWLEDGEMENTS This work is financially supported by the

National Natural Science Foundation of China (51503178, 51631001, 51590882), National Key R&D Program of China (2017YFA0206301, 2016 YFA0200102) and Natural Science Foundation of Beijing

Municipality (219001). We also thank Professor Ping Xu from Harbin Institute of Technology, Professor Guangjie Shao, Professor Zhisheng Zhao, Mr. Hongchao Wang from Yanshan University for

their help with the electrochemical, XRD and BET analysis. AUTHOR INFORMATION AUTHORS AND AFFILIATIONS * State Key Laboratory of Metastable Materials Science and Technology, Yanshan

University, 066004, Qinhuangdao, China Kesong Tian, Wanchun Guo, Xueai Li, Zhaopeng Xu & Haiyan Wang * Beijing Innovation Center for Engineering Science and Advanced Technology

(BIC-ESAT), College of Engineering, Peking University, 100871, Beijing, China Kesong Tian, Wei Li & Yanglong Hou * Hebei Key Laboratory of Applied Chemistry, College of Environmental and

Chemical Engineering, Yanshan University, 066004, Qinhuangdao, China Kesong Tian, Junyan Wang, Ling Cao, Wei Yang, Wanchun Guo, Fengyan Wang, Xueai Li & Haiyan Wang * Institute of High

Energy Physics, Chinese Academy of Sciences, 100049, Beijing, China Shuhu Liu * School of Chemistry and Chemical Engineering, Harbin Institute of Technology, 150080, Harbin, China Zhenbo

Wang Authors * Kesong Tian View author publications You can also search for this author inPubMed Google Scholar * Junyan Wang View author publications You can also search for this author

inPubMed Google Scholar * Ling Cao View author publications You can also search for this author inPubMed Google Scholar * Wei Yang View author publications You can also search for this

author inPubMed Google Scholar * Wanchun Guo View author publications You can also search for this author inPubMed Google Scholar * Shuhu Liu View author publications You can also search for

this author inPubMed Google Scholar * Wei Li View author publications You can also search for this author inPubMed Google Scholar * Fengyan Wang View author publications You can also search

for this author inPubMed Google Scholar * Xueai Li View author publications You can also search for this author inPubMed Google Scholar * Zhaopeng Xu View author publications You can also

search for this author inPubMed Google Scholar * Zhenbo Wang View author publications You can also search for this author inPubMed Google Scholar * Haiyan Wang View author publications You

can also search for this author inPubMed Google Scholar * Yanglong Hou View author publications You can also search for this author inPubMed Google Scholar CONTRIBUTIONS K.T., W.G., Y.H.,

and H.W. conceived the concept, designed the experiments, analyzed the experimental data, discussed the related results, and wrote the manuscript. K.T., J.W., L.C., and W.Y. synthesized the

resins and the corresponding nitrogen-doped carbon materials and performed electrochemical measurements. S.L. analyzed N K edge XAFS spectrum of the samples. W.L., F.W., X.L., and Z.X.

performed Raman, TEM, and XRD analysis. Z.W. performed some electrochemical analysis. CORRESPONDING AUTHORS Correspondence to Wanchun Guo, Haiyan Wang or Yanglong Hou. ETHICS DECLARATIONS

COMPETING INTERESTS The authors declare no competing interests. ADDITIONAL INFORMATION PEER REVIEW INFORMATION _Nature Communications_ thanks the anonymous reviewers for their contribution

to the peer review of this work. Peer reviewer reports are available. PUBLISHER’S NOTE Springer Nature remains neutral with regard to jurisdictional claims in published maps and

institutional affiliations. SUPPLEMENTARY INFORMATION SUPPLEMENTARY INFORMATION PEER REVIEW FILE SOURCE DATA SOURCE DATA RIGHTS AND PERMISSIONS OPEN ACCESS This article is licensed under a

Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit

to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are

included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and

your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this

license, visit http://creativecommons.org/licenses/by/4.0/. Reprints and permissions ABOUT THIS ARTICLE CITE THIS ARTICLE Tian, K., Wang, J., Cao, L. _et al._ Single-site

pyrrolic-nitrogen-doped _sp_2-hybridized carbon materials and their pseudocapacitance. _Nat Commun_ 11, 3884 (2020). https://doi.org/10.1038/s41467-020-17727-y Download citation * Received:

04 September 2019 * Accepted: 16 July 2020 * Published: 04 August 2020 * DOI: https://doi.org/10.1038/s41467-020-17727-y SHARE THIS ARTICLE Anyone you share the following link with will be

able to read this content: Get shareable link Sorry, a shareable link is not currently available for this article. Copy to clipboard Provided by the Springer Nature SharedIt content-sharing

initiative