Highly conductive and stretchable conductors fabricated from bacterial cellulose

ABSTRACT Advanced materials that can remain electrically conductive under substantial elastic stretch and bending have attracted extensive interest recently owing to their broad application

potentials, particularly for flexible electronics. Here, we have developed a simple and inexpensive method to fabricate highly conductive and stretchable composites using bacterial cellulose

(BC) pellicles as starting materials, which can be produced in large amounts on an industrial scale via a microbial fermentation process. The prepared pyrolyzed BC

(p-BC)/polydimethylsiloxane (PDMS) composites exhibit a high electrical conductivity of 0.20–0.41 S cm−1, which is much higher than conventional carbon nanotubes and graphene-based

composites. More importantly, the p-BC/PDMS composites that combine high stretchability with high conductivity show great electromechanical stability. Even after 1000 stretching cycles at

the maximum strain of 80%, the resistance of the composites increased by only ∼10%. The resistance increased slightly (∼4%) after 5000 bending cycles with a maximum bending radius of 1.0 mm.

SIMILAR CONTENT BEING VIEWED BY OTHERS ULTRASTRONG AND FATIGUE-RESISTANT BIOINSPIRED CONDUCTIVE FIBERS VIA THE IN SITU BIOSYNTHESIS OF BACTERIAL CELLULOSE Article Open access 31 March 2023

STRONG AND HIGH-CONDUCTIVITY HYDROGELS WITH ALL-POLYMER NANOFIBROUS NETWORKS FOR APPLICATIONS AS HIGH-CAPACITANCE FLEXIBLE ELECTRODES Article Open access 09 September 2024 TOWARD IMPROVED

TRADE-OFF BETWEEN THERMOELECTRIC AND MECHANICAL PERFORMANCES IN POLYCARBONATE/SINGLE-WALLED CARBON NANOTUBE COMPOSITE FILMS Article Open access 02 October 2020 INTRODUCTION Although they

possess high conductivity, conventional metal conductors cannot meet the demands for some emerging applications, particularly for flexible electronic devices,1, 2, 3 actuators,4 sensors5, 6

and loudspeakers.7 These limitations have motivated intensive efforts to develop advanced electrically conductive materials capable of substantial elastic stretching and bending.2, 8, 9, 10,

11 One method for fabricating stretchable conductors is to form one dimensional ‘wavy’ inorganic ribbons or two dimensional ‘wavy’ membranes by releasing pre-strained elastomeric substrates

with conductive materials lying on them.9, 12, 13, 14, 15, 16 Such wavy conductive structures have exhibited excellent conductivity and mechanical stretchability. Another method is to embed

or bond rigid and active electronic components into a soft rubbery polymer.2, 10, 17, 18, 19, 20 For example, Shin _et al._17 fabricated elastomeric conductive composites by the

infiltration of multiwalled carbon nanotube forests with a polyurethane binder. Someya’s group developed highly conductive, printable and stretchable composite films using ionic liquid,

fluorinated copolymer and ultralong single-walled carbon nanotubes (SWNTs).1, 2 Transparent stretchable conductors have also been fabricated by embedding well-aligned carbon nanotube (CNT)

ribbons or graphene films in polydimethylsiloxane (PDMS).11, 19 Although mechanical stretchability was successfully achieved, most of the above studies demonstrated that the resistance of

the obtained composites increases rapidly with tensile strain (>100% increase of resistance at 100% strain).5, 10, 11, 17, 18 Very recently, a new strategy was developed for generating

stretchable conductors by backfilling an infinite connected network of conducting fillers (such as single-walled carbon nanotubesaerogels21 or graphene foams22) with an elastic polymer.

Owing to the prefabricated three dimensional (3D) network structures, these composites showed a relatively high electrical conductivity and electromechanical stability under stretching and

bending.21, 22 However, the cost of single-walled carbon nanotubes and graphene fabricated from the chemical vapor deposition process is still high. It is quite desirable to explore

inexpensive, green and scalable processes to lower the fabrication cost for industrial applications. Bacterial cellulose (BC) has long been used as the raw material of _nata-de-coco_, an

indigenous dessert food of the Philippines, for which one centimeter thick gel sheets fermented with coconut-water are cut into cubes and immersed in sugar sirup.23 BC can be produced in

large amounts on an industrial scale via a microbial fermentation process.23, 24 It is well known that BC pellicles are composed of interconnected 3D networks of nanofibers that have a

native cellulose I crystal structure with high-molar-mass, hydrogen-bonded polymer chains in an extended-chain conformation.23, 25 In addition, BC has been used as a precursor material to

prepare graphitized films26 and carbon nanofibers.27 Inspired by this biomaterial,28, 29 we propose to construct 3D conductive carbon nanofiber networks from BC pellicles for fabricating

stretchable conductors. The major advantages of using BC as a precursor material include easy fabrication, low cost and its mechanically robust 3D network structures, which is a key point

for the electromechanical performance of the final composites. In this paper, we demonstrate that BC pellicles can be employed as starting materials for fabricating stretchable conductors.

The prepared pyrolyzed BC (p-BC)/PDMS composites exhibit a high conductivity and extraordinary electromechanical stability even under high stretching and bending strain. MATERIALS AND

METHODS MATERIALS Purified BC pellicles with fiber content of ∼1% (vol/vol) were kindly provided by Ms CY Zhong (Hainan Yeguo Foods Co., Ltd., Hainan, China). The fibers were produced by the

bacterial strain _Acetobacter xylinum_ using a culture of coconut milk and sucrose.24 Sylgard 184 silicone elastomer base and curing agent were purchased from Dow Corning (Midland, MI,

USA). METHODS The BC pellicles were first cut into rectangular or cubic shapes with a sharp blade, frozen in liquid nitrogen (–196 °C) and then freeze-dried in a bulk tray dryer (Labconco

Corporation, Kansas City, MO, USA) at a sublimating temperature of –48 °C and a pressure of 0.04 mbar. The obtained BC aerogels were then pyrolyzed under flowing argon at 600–1450 °C to

generate black and ultralight p-BC aerogels. The p-BC/PDMS composites were fabricated by infiltrating the p-BC aerogels with PDMS pre-polymer, a viscous mixture of base/curing agent (Sylgard

184, Dow Corning), followed by degassing in a vacuum oven for 2 h and thermally curing at 70 °C for 1 h. CHARACTERIZATION The electrical conductivity of p-BC aerogels and p-BC/PDMS

composites was measured by a two-probe method with the PM5 Analytical Probe System (Cascade Microtech, Inc., Beaverton, OR, USA) and Keithley 4200 SCS at room temperature in air. Copper

wires were embedded and connected to the p-BC aerogels with silver paste (Dupont 4929N, DuPont Corporation, Wilmington, DE, USA) before infiltration with PDMS pre-polymer. The compressive

tests of the BC and p-BC aerogels were performed by using an Instron 5565A, equipped with two flat-surface compression stages and 500 N load cells. The strain ramp rate was maintained at 10 

mm per min for all of the tests. The sample size was measured using a standard caliper. Scanning electron microscopy was performed with a field emission scanning electron microanalyzer

(Zeiss Supra 40, Carl Zeiss AG, Baden-Wurttemberg, Oberkochen, Germany) after coating the samples with an Au layer of approximately 3 nm using a Sputter Coater (Model BAL-TEC SCD 005).

RESULTS AND DISCUSSION Figure 1a describes the synthetic pathway. A piece of purified BC pellicle with the size of 200 × 230 × 4 mm3 was first cut into a rectangular shape with a sharp blade

(step 1). To prevent the collapse of the gel network, a freeze-drying technique was used to remove the water from the small piece of BC pellicle to form a porous cellulose nanofibrous

aerogel (step 2). The dried BC aerogel was then pyrolyzed under flowing argon at 600–1450 °C to generate a black, ultralight and conductive aerogel (step 3). For measuring the mechanical

properties of aerogels, another BC pellicle with a thickness of 12 mm was cut into a cubic shape, freeze-dried and pyrolyzed (Supplementary Figure S1). The apparent density of the dried BC

aerogels was ∼7 mg cm−3. The porosity was estimated to be 99.56% based on calculations using a density of 1.6 g cm−3 for the cellulose nanofibrils.25 During the pyrolysis process, the BC

sample gradually shrank to half of its original size in three dimensions, whereas the volume shrank by ∼88%. The obtained p-BC aerogels are extremely light, and have an ultralow density of

3–4 mg cm−3 with a high porosity of >99.7%. Scanning electron microscopy images of the freeze-dried BC aerogel reveal a highly porous network structure consisting of numerous nanofibers

(Figure 1b). High-magnification scanning electron microscopy observation indicates that these nanofibers with a diameter of 20–50 nm are highly interconnected with large numbers of junctions

(Supplementary Figure S2).25 After a pyrolysis treatment, the p-BC aerogels obtain a 3D network structure, except that the fiber diameter is decreased to 10–20 nm (Figure 1c) due to the

carbonization of the BC and evaporation of volatile species such as CO, CO2, methanol, and acetic acid during pyrolysis.27 We propose that this unique 3D network structure is responsible for

the outstanding mechanical and conducting properties of the p-BC aerogels (see below for details). Unlike conventional low-density aerogels that are brittle and tend to break even upon a

small compression, the present BC and p-BC aerogels composed of interconnected nanofibers exhibited high flexibility, that is, suppression of brittleness. The compressive properties of the

BC-based aerogels were studied quantitatively, and the results are shown in Figures 2a and b. The BC aerogels can be compressed without disintegration after being subject to a maximum strain

of 80% with a compressive strength of 18.0 kPa (Figure 2a). When the compressive load was removed, the BC aerogel did not return to its original shape because of the strongly interacting

surface hydroxyl groups in the BC nanofibers (the inset in Figure 2a). In contrast, the p-BC aerogel showed a highly elastic compressibility and almost completely recovered its original

volume after the compression was released (Figure 2b and inset), although it had a much lower compressive strength of 2.5 kPa at 80% strain, most likely due to the reduced density after

pyrolysis treatment. The p-BC aerogel was subjected to a fatigue cyclic compression test (ɛ=80%) by undergoing 100 loading/unloading cycles (Figure 2b). The unloading curves show that the

stresses remained above zero until ɛ=0, suggesting almost complete recovery of the compressed aerogel and no thickness reduction after the fatigue test. The degradation at the maximum

compressive strength (at 80% strain) of the p-BC aerogel was only 7.5% after 100 cycles. It is believed that the robust mechanical properties of the p-BC aerogel are attributed to its unique

interconnected 3D network structures and elimination of the hydrogen-bond interaction during pyrolysis. The flexible p-BC/PDMS composites were prepared by infiltrating the p-BC aerogels

with the polymer resin (Dow Corning Sylgard 184) under vacuum before curing at 70 °C (the inset in Figure 2c). The dimensions of the aerogels remained unchanged after infiltrating and

curing. Scanning electron microscopy images of the fracture surface of the composites show that the carbon nanofibers are homogenously distributed throughout the polymer matrix (Figure 2c

and Supplementary Figure S3). The electric resistance of the p-BC aerogels and their composites with PDMS were measured by the two-probe method. All of the measured current–voltage (I–V)

curves showed a linear dependence, indicating good ohmic contacts between the composites and the electrodes (Supplementary Figure S4). The results show that the electrical conductivity of

the p-BC/PDMS composites was approximately equal to that of the initial p-BC aerogels (Supplementary Figure S4), indicating that introduction of the PDMS matrix does not damage the

interconnected 3D network of carbon nanofibers. In addition, the electrical conductivity of the p-BC aerogels and p-BC/PDMS composites increases rapidly with the pyrolysis temperature

(Figure 2d) because higher temperature results in carbon nanofibers with a higher degree of graphitization.27 The composites show an electrical conductivity of >0.2 S cm−1 when the

pyrolysis temperature is >1000 °C despite the very low loading of the active electronic component (< 0.3 vol%). The electrical conductivity of the composite made from the BC aerogel

that was pyrolyzed at 1450 °C reached 0.41 S cm−1, which is much higher than traditional CNTs and graphene-based composites prepared by solution mixing with such a low filler content

(Supplementary Table S1). For the latter, electronically active fillers, such as CNTs and graphene nanosheets, are embedded separately in the polymer matrix, and the electrical conductivity

of these composites is strongly dependent on the electron percolation between the filler particles.30, 31 In contrast, in our composites, because the infinite interconnected network of

conductive carbon nanofibers remained unchanged even after infiltrating with an insulating polymer, electrons can move very quickly through the network it, resulting in a higher electrical

conductivity. When compared with the present method, the solution mixing method exhibits more versatility, such as allowing for easy control of the filler content, but the electrical

conductivity of the composite obtained by solution mixing can only be controlled in a limited range because high filler content likely results in phase disengagement and fails to form

mechanically robust composites. We also measured the stress-strain curves of the p-BC/PDMS composites and pure PDMS, and the results are shown in Supplementary Figure S5. The fabricated

p-BC/PDMS composite exhibited high stretchability with a strain-to-failure rate of 118%, which is somewhat lower than that of the pure PDMS sheet (∼150%). The extraordinary electrical

conductivity of the p-BC/PDMS composites, as well as their good mechanical properties, indicates a great potential as flexible and stretchable conductors (Figure 3). We evaluated the

stretchability and foldability of the composite conductors by measuring resistances with respect to stretching strain and bending radii, which were carried out with a high-precision

mechanical system (Instron 5565A). The composite fabricated from the BC aerogel that was pyrolyzed at 1300 °C was tested and had an initial conductivity of 0.33 S cm−1. The composites

remained robust after repeated stretching–releasing cycles and bending. We first investigated the resistance variation as a function of uniaxial tensile strain from 0 to 80% (Figures 3a and

b). Note that the composite remained conductive until it broke at 118% strain (Supplementary Figure S6). During the first cycle of stretching–releasing, the resistance of p-BC/PDMS composite

increased nearly linearly with increasing tensile strain (Figure 3a). The resistance increase (_ΔR_/_R_0) at the maximum strain (80%) is 14.8%, which is much lower than the reported values

for conventional graphene- and CNT-based stretchable conductors2, 10, 11, 18 and is comparable to that of emerging single-walled carbon nanotubes/PDMS21 and graphene foam/PDMS22 composites.

When the stretched composite was released to the unstrained state, we observed 9.2% loss in conductivity, implying a partial breaking or cracking of the nanofibrous network. We then

performed a second stretching cycle, where the _ΔR_/_R_0 at the maximum strain was the same as that during the first cycle, and only another 0.3% loss in conductivity was observed when the

strain was fully released (Figure 3a). In fact, except for the first cycle, the resistance showed no obvious change between each stretching–releasing cycle. The p-BC/PDMS composite reached a

stable _ΔR_/_R_0 after five stretching–releasing cycles and showed great reversibility thereafter (the inset in Figure 3b). It is worth mentioning that there was only 0.8% increase in the

_ΔR_/_R_0 from the first to the thousandth cycle (Figure 3b), which shows the excellent electromechanical properties of the present composites. We also investigated the resistance variation

under bending deformations, as shown in Figures 3c and d. During the first bending cycle, the resistance showed a slight increase of 2.0% at a bending radius of 1.0 mm and could recover

partially after unbending (Figure 3c), similar to the results in the stretching tests. As the number of bending cycles increased, the resistance variation of composites gradually became

stable, and the resistance increased only by 4.1% even after 5 000 cycles for a bend radius of 1.0 mm (Figure 3b and inset). A simple device was demonstrated for lighting a commercial LED

using the p-BC/PDMS composites. As shown in Supplementary Figure S7, the brightness of the LED did not change significantly when the p-BC/PDMS composite was twisted or stretched. These

results show the extraordinary electromechanical stability of p-BC/PDMS composites and their great potential for high-performance stretchable and flexible conductors. We suspect that the

outstanding electromechanical properties of the composites result from the 3D network structures of the p-BC aerogels and their robust mechanical properties, as revealed in Figure 2b.

Because the robust interconnected 3D network of carbon nanofibers was preformed and remained unchanged after infiltrating with PDMS, the conductive nanofibers within the composite could

slide past one other without losing junction points while being supported by the PDMS during stretching and bending; thus little variation in conductivity was observed. CONCULUSIONS In

summary, we have developed a new type of highly conductive and stretchable conductors using an inexpensive and green material, BC pellicles, as a precursor, which can be produced in large

amounts on an industrial scale via a microbial fermentation process. The prepared pyrolyzed p-BC/PDMS composites with a high electrical conductivity of 0.20–0.41 S cm−1 exhibit extraordinary

electromechanical stability even under high tensile and bending strain. It is believed that the outstanding electromechanical properties of the composites are due to the robust and

preformed 3D networks of the p-BC aerogels that provide an interconnected pathway through which electrons can quickly move. Because of the advantages of the present method, such as

inexpensive and accessible precursor material and easy fabrication, it is possible to scale up the fabrication process for industrial applications in large-scale flexible, stretchable and

foldable electronics. REFERENCES * Sekitani, T., Nakajima, H., Maeda, H., Fukushima, T., Aida, T., Hata, K. & Someya, T. Stretchable active-matrix organic light-emitting diode display

using printable elastic conductors. _Nat. Mater._ 8, 494–499 (2009). Article  CAS  Google Scholar  * Sekitani, T., Noguchi, Y., Hata, K., Fukushima, T., Aida, T. & Someya, T. A

rubberlike stretchable active matrix using elastic conductors. _Science_ 321, 1468–1472 (2008). Article  CAS  Google Scholar  * Pang, S., Hernandez, Y., Feng, X. & Müllen, K. Graphene as

transparent electrode material for organic electronics. _Adv. Mater._ 23, 2779–2795 (2011). Article  CAS  Google Scholar  * Koerner, H., Price, G., Pearce, N. A., Alexander, M. & Vaia,

R. A. Remotely actuated polymer nanocomposites—stress-recovery of carbon-nanotube-filled thermoplastic elastomers. _Nat. Mater._ 3, 115–120 (2004). Article  CAS  Google Scholar  * Lipomi, D.

J., Vosgueritchian, M., Tee, B. C. K., Hellstrom, S. L., Lee, J. A., Fox, C. H. & Bao, Z. Skin-like pressure and strain sensors based on transparent elastic films of carbon nanotubes.

_Nat. Nanotechnol._ 6, 788–792 (2011). Article  CAS  Google Scholar  * Someya, T., Sekitani, T., Iba, S., Kato, Y., Kawaguchi, H. & Sakurai, T. A large-area, flexible pressure sensor

matrix with organic field-effect transistors for artificial skin applications. _Proc. Natl Acad. Sci. USA_ 101, 9966–9970 (2004). Article  CAS  Google Scholar  * Xiao, L., Chen, Z., Feng,

C., Liu, L., Bai, Z.-Q., Wang, Y., Qian, L., Zhang, Y., Li, Q., Jiang, K. & Fan, S. Flexible, stretchable, transparent carbon nanotube thin film loudspeakers. _Nano Lett._ 8, 4539–4545

(2008). Article  CAS  Google Scholar  * Rogers, J. A., Someya, T. & Huang, Y. Materials and mechanics for stretchable electronics. _Science_ 327, 1603–1607 (2010). Article  CAS  Google

Scholar  * Khang, D.-Y., Jiang, H., Huang, Y. & Rogers, J. A. A stretchable form of single-crystal silicon for high-performance electronics on rubber substrates. _Science_ 311, 208–212

(2006). Article  CAS  Google Scholar  * Chun, K. Y., Oh, Y., Rho, J., Ahn, J. H., Kim, Y. J., Choi, H. R. & Baik, S. Highly conductive, printable and stretchable composite films of

carbon nanotubes and silver. _Nat. Nanotechnol_ 5, 853–857 (2010). Article  CAS  Google Scholar  * Kim, K. S., Zhao, Y., Jang, H., Lee, S. Y., Kim, J. M., Ahn, J. H., Kim, P., Choi, J. Y.

& Hong, B. H. Large-scale pattern growth of graphene films for stretchable transparent electrodes. _Nature_ 457, 706–710 (2009). Article  CAS  Google Scholar  * Bowden, N., Brittain, S.,

Evans, A. G., Hutchinson, J. W. & Whitesides, G. M. Spontaneous formation of ordered structures in thin films of metals supported on an elastomeric polymer. _Nature_ 393, 146–149

(1998). Article  CAS  Google Scholar  * Lacour, S. P., Wagner, S., Huang, Z. Y. & Suo, Z. Stretchable gold conductors on elastomeric substrates. _Appl. Phys. Lett._ 82, 2404–2406 (2003).

Article  CAS  Google Scholar  * Kim, D.-H., Xiao, J., Song, J., Huang, Y. & Rogers, J. A. Stretchable, curvilinear electronics based on inorganic materials. _Adv. Mater._ 22, 2108–2124

(2010). Article  CAS  Google Scholar  * Wang, X. L., Hu, H., Shen, Y. D., Zhou, X. C. & Zheng, Z. J. Stretchable conductors with ultrahigh tensile strain and stable metallic conductance

enabled by prestrained polyelectrolyte nanoplatforms. _Adv. Mater._ 23, 3090–3094 (2011). Article  CAS  Google Scholar  * Zhu, Y. & Xu, F. Buckling of aligned carbon nanotubes as

stretchable conductors: a new manufacturing strategy. _Adv. Mater._ 24, 1073–1077 (2012). Article  CAS  Google Scholar  * Shin, M. K., Oh, J., Lima, M., Kozlov, M. E., Kim, S. J. &

Baughman, R. H. Elastomeric conductive composites based on carbon nanotube forests. _Adv. Mater._ 22, 2663–2667 (2010). Article  CAS  Google Scholar  * Yu, Z., Niu, X., Liu, Z. & Pei, Q.

Intrinsically stretchable polymer light-emitting devices using carbon nanotube-polymer composite electrodes. _Adv. Mater._ 23, 3989–3994 (2011). Article  CAS  Google Scholar  * Zhang, Y.,

Sheehan, C. J., Zhai, J., Zou, G., Luo, H., Xiong, J., Zhu, Y. T. & Jia, Q. X. Polymer-embedded carbon nanotube ribbons for stretchable conductors. _Adv. Mater._ 22, 3027–3031 (2010).

Article  CAS  Google Scholar  * Jung, Y. J., Kar, S., Talapatra, S., Soldano, C., Viswanathan, G., Li, X., Yao, Z., Ou, F. S., Avadhanula, A., Vajtai, R., Curran, S., Nalamasu, O. &

Ajayan, P. M. Aligned Carbon nanotube−polymer hybrid architectures for diverse flexible electronic applications. _Nano Lett._ 6, 413–418 (2006). Article  CAS  Google Scholar  * Kim, K. H.,

Vural, M. & Islam, M. F. Single-walled carbon nanotube aerogel-based elastic conductors. _Adv. Mater._ 23, 2865–2869 (2011). Article  CAS  Google Scholar  * Chen, Z., Ren, W., Gao, L.,

Liu, B., Pei, S. & Cheng, H.-M. Three-dimensional flexible and conductive interconnected graphene networks grown by chemical vapour deposition. _Nat. Mater._ 10, 424–428 (2011). Article

  CAS  Google Scholar  * Iguchi, M., Yamanaka, S. & Budhiono, A. Bacterial cellulose—a masterpiece of nature's arts. _J. Mater. Sci._ 35, 261–270 (2000). Article  CAS  Google

Scholar  * China Patent. A microbial fermentation process for fabricating dietary fiber by using coconut water as raw materials, ZL96100534.3 (2001). * Yano, H., Sugiyama, J., Nakagaito, A.

N., Nogi, M., Matsuura, T., Hikita, M. & Handa, K. Optically transparent composites reinforced with networks of bacterial nanofibers. _Adv. Mater._ 17, 153–155 (2005). Article  CAS 

Google Scholar  * Yoshino, K., Matsuoka, R., Nogami, K., Yamanaka, S., Watanabe, K., Takahashi, M. & Honma, M. Graphite film prepared by pyrolysis of bacterial cellulose. _J. Appl.

Phys._ 68, 1720–1725 (1990). Article  CAS  Google Scholar  * Wan, Y. Z., Zuo, G. F., Yu, F., Huang, Y. A., Ren, K. J. & Luo, H. L. Preparation and mineralization of three-dimensional

carbon nanofibers from bacterial cellulose as potential scaffolds for bone tissue engineering. _Surf. Coat. Technol._ 205, 2938–2946 (2011). Article  CAS  Google Scholar  * Wang, J., Cheng,

Q. & Tang, Z. Layered nanocomposites inspired by the structure and mechanical properties of nacre. _Chem. Soc. Rev._ 41, 1111–1129 (2012). Article  Google Scholar  * Cheng, Q., Li, M.,

Jiang, L. & Tang, Z. Bioinspired layered composites based on flattened double-walled carbon nanotubes. _Adv. Mater._ 24, 1838–1843 (2012). Article  CAS  Google Scholar  * Kuilla, T.,

Bhadra, S., Yao, D. H., Kim, N. H., Bose, S. & Lee, J. H. Recent advances in graphene based polymer composites. _Prog. Polym. Sci._ 35, 1350–1375 (2010). Article  CAS  Google Scholar  *

Spitalsky, Z., Tasis, D., Papagelis, K. & Galiotis, C. Carbon nanotube-polymer composites: chemistry, processing, mechanical and electrical properties. _Prog. Polym. Sci._ 35, 357–401

(2010). Article  CAS  Google Scholar  Download references ACKNOWLEDGEMENTS SHY acknowledge special funding support from the National Basic Research Program of China (Grant 2010CB934700), the

National Natural Science Foundation of China (Grants 91022032, 21061160492, J1030412), the Chinese Academy of Sciences (Grant KJZD-EW-M01-1), the International Science & Technology

Cooperation Program of China (Grant 2010DFA41170), and the Principal Investigator Award by the National Synchrotron Radiation Laboratory at the USTC. HWL acknowledge Fundamental Research

Funds for the Central Universities. _Author contributions:_ SHY conceived the project and planned the experiments. HWL and QFG prepared samples and carried out the characterizations. SHY and

HWL analyzed the data and wrote the paper. All authors discussed the results and commented on the paper. AUTHOR INFORMATION AUTHORS AND AFFILIATIONS * Division of Nanomaterials and

Chemistry, Department of Chemistry, Hefei National Laboratory for Physical Sciences at the Microscale (HFNL), The National Synchrotron Radiation Laboratory, University of Science and

Technology of China (USTC), Hefei, Anhui, PR China Hai-Wei Liang, Qing-Fang Guan, Zhu- Zhu, Lu-Ting Song, Hong-Bin Yao, Xuan Lei & Shu-Hong Yu Authors * Hai-Wei Liang View author

publications You can also search for this author inPubMed Google Scholar * Qing-Fang Guan View author publications You can also search for this author inPubMed Google Scholar * Zhu- Zhu View

author publications You can also search for this author inPubMed Google Scholar * Lu-Ting Song View author publications You can also search for this author inPubMed Google Scholar *

Hong-Bin Yao View author publications You can also search for this author inPubMed Google Scholar * Xuan Lei View author publications You can also search for this author inPubMed Google

Scholar * Shu-Hong Yu View author publications You can also search for this author inPubMed Google Scholar CORRESPONDING AUTHOR Correspondence to Shu-Hong Yu. ETHICS DECLARATIONS COMPETING

INTERESTS The authors declare no conflicts of interest. ADDITIONAL INFORMATION Supplementary Information accompanies the paper on the NPG Asia Materials website SUPPLEMENTARY INFORMATION

SUPPLEMENTARY INFORMATION (DOC 1631 KB) RIGHTS AND PERMISSIONS This work is licensed under the Creative Commons Attribution-NonCommercial-No Derivative Works 3.0 Unported License. To view a

copy of this license, visit http://creativecommons.org/licenses/by-nc-nd/3.0/ Reprints and permissions ABOUT THIS ARTICLE CITE THIS ARTICLE Liang, HW., Guan, QF., Zhu, Z. _et al._ Highly

conductive and stretchable conductors fabricated from bacterial cellulose. _NPG Asia Mater_ 4, e19 (2012). https://doi.org/10.1038/am.2012.34 Download citation * Received: 23 March 2012 *

Revised: 25 April 2012 * Accepted: 30 April 2012 * Published: 01 June 2012 * Issue Date: June 2012 * DOI: https://doi.org/10.1038/am.2012.34 SHARE THIS ARTICLE Anyone you share the following

link with will be able to read this content: Get shareable link Sorry, a shareable link is not currently available for this article. Copy to clipboard Provided by the Springer Nature

SharedIt content-sharing initiative KEYWORDS * aerogels * bacterial cellulose * carbon nanofibers * electrical conductivity * pyrolysis * stretchable conductors